OK Flux 10.71
OK Flux 10.71 is a neutral, bonded flux intended primarily for multipass butt and fillet welding of carbon and low alloy steels. It combines outstanding welding performance with excellent weld properties. OK Flux 10.71 is suitable for use with AC and DC, single and multiwire systems at currents up to 1000 amps. It should not be used in applications where there is heavy rust or mill scale on the base plate. Among the many areas where OK 10.71 is used are general structural welding, bridge fabrication, heavy equipment fabrication, and line pipe welding.
Classifications
Classifications |
AWS A5.17 : F7P5- EH12K AWS A5.17 : F7P4-EM14K AWS A5.17 : F7A5-EH12K AWS A5.17 : F7A4-EM13K AWS A5.17 : F7A4-EM12K AWS A5.17 : F7A2-EM14K AWS A5.23 : F8A4-ENi1K-Ni1 |
Approvals
Approvals |
CE EN 13479 CWB AWS A5.23 F9A6-ENi4-Ni4-H8 CWB AWS A5.23 F8A4-ENi1K-Ni1-H8 CWB CSA W48 F49A4-EM12K-H8 DB 51.039.05 NAKS/HAKC RD 03-613-03 |
Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
Slag Type | Aluminate-basic |
Grain Size | 0.2-1.6 mm (10x65 mesh) or 0.315 -2.0 mm (9x48 mesh) |
Diffusible Hydrogen | max 5 ml H/100g weld metal (Redried flux) |
Density | nom: 1.2 kg/dm3 |
Basicity Index | nom: 1.5 |
Alloy Transfer | Slightly Silicon and moderately Manganese alloying |
Flux Consumption
Volts | kg Flux / kg Wire DC+ | kg Flux / kg Wire AC |
26 V | 0.7 kg | 0.6 kg |
30 V | 1.0 kg | 0.9 kg |
34 V | 1.3 kg | 1.2 kg |
38 V | 1.6 kg | 1.4 kg |
Amps | Dimensions | Travel speed |
580 A | Ø 4.0 mm | 55 cm/min |
Classifications
Wire | AWS/EN | AWS - As Welded | AWS - PWHT |
Spoolarc 81 | AWS A5.17: EM12K | F7A4-EM12K | |
Spoolarc 75 | AWS A5.23: ENi1K | F8A-ENi1K-Ni1 | |
Spoolarc 71 | AWS A5.17: EM14K | F7A2-EM14K | F7P4-EM14K |
Spoolarc 29S | AWS A5.17: EM13K | F7A4-EM13K | |
Spoolarc 53 | AWS A5.17: EH12K | F7A5-EH12K | F7P5-EH12K |
Approvals
Wire | ABS | BV | CE | ClassNK | DB | DNV | GL | LR | PRS | RINA | RS | VdTÜV |
OK Autrod 12.10 | * | * | * | - | * | * | * | * | * | - | * | * |
OK Autrod 12.20 | * | * | * | - | * | * | * | * | * | * | * | * |
OK Autrod 12.22 | * | * | * | * | * | * | * | * | - | - | * | * |
OK Autrod 12.24 | * | * | * | * | * | * | * | * | * | * | * | * |
OK Autrod 12.30 | - | - | * | - | * | - | - | - | - | - | - | * |
OK Autrod 12.32 | - | - | * | - | * | - | - | - | - | - | - | * |
OK Autrod 13.27 | - | - | - | - | - | - | - | - | - | - | - | * |
OK Autrod 13.36 | - | - | * | - | - | - | - | - | - | - | - | - |
*Selected production units only. Please contact ESAB for more information. Visit esab.com to download specific flux/wire combination fact sheets for more details. |
Typical Mechanical Properties
Wire | Condition | Yield Strength | Tensile Strength | Charpy V-Notch | Elongation | Testing Time |
Spoolarc 29S | As Welded null | 505 MPa (73 ksi) |
600 MPa (87 ksi) |
41 J @ -40°C, (30 ft-lb @ -40 °F) |
30 % | |
Spoolarc 53 | As Welded null | 530 MPa (77 ksi) |
625 MPa (91 ksi) |
61 J @ -46°C, (45 ft-lb @ -50 °F) |
28 % | |
Spoolarc 53 | Stress Relieved 621C (1150F) | 448 MPa (65 ksi) |
545 MPa (79 ksi) |
108 J @ -46°C, (80 ft-lb @ -50 °F) |
32 % | 1 hr |
Spoolarc 71 | As Welded null | 525 MPa (76 ksi) |
600 MPa (87 ksi) |
67 J @ -29°C, (48 ft-lb @ -20 °F) |
27 % | |
Spoolarc 71 | Stress Relieved 621C (1150F) | 510 MPa (74 ksi) |
625 MPa (91 ksi),635 MPa (92 ksi) |
47 J @ -40°C, (35 ft-lb @ -40 °F) 51 J @ -40°C, (38 ft-lb @ -40 °F) |
30 % | 8 hr,1 hr |
Spoolarc 75 | As Welded null | 540 MPa (78 ksi) |
625 MPa (91 ksi) |
58 J @ -40°C, (43 ft-lb @ -40 °F) |
28 % | |
Spoolarc 81 | As Welded null | 470 MPa (68 ksi) |
560 MPa (81 ksi) |
60 J @ -40°C, (44 ft-lb @ -40 °F) |
30 % |
Typical Weld Metal Analysis %
Typical Weld Metal Analysis % | ||||||||||||||
C | Mn | Ni | P | S | Si | |||||||||
As Welded Spoolarc 29S | ||||||||||||||
0.06 % | 1.80 % | - | 0.014 % | 0.007 % | 0.80 % | |||||||||
As Welded Spoolarc 53 | ||||||||||||||
0.07 % | 1.80 % | - | 0.022 % | 0.010 % | 0.50 % | |||||||||
As Welded Spoolarc 71 | ||||||||||||||
0.06 % | 1.70 % | - | 0.018 % | 0.009 % | 0.60 % | |||||||||
As Welded Spoolarc 75 | ||||||||||||||
0.07 % | 1.70 % | 0.90 % | 0.016 % | 0.012 % | 0.70 % | |||||||||
As Welded Spoolarc 81 | ||||||||||||||
0.07 % | 1.50 % | - | 0.020 % | 0.011 % | 0.50 % |